Description:

Type 201 Stainless Steel is an austenitic chromium-nickel-manganese stainless steel which was developed to conserve nickel. Type 201 is a lower cost alternative to conventional Cr-Ni stainless steels such as 301 and 304. Nickel is replaced by additions of manganese and nitrogen. It is non-hardenable by thermal treatment, but may be cold worked to high tensile strengths. Type 201 is essentially nonmagnetic in the annealed condition and becomes magnetic when cold worked. Type 201 can be substituted for Type 301 in many applications.

Product Forms:

Sheet, Strip

Specifications:

ASTM A240, A666

Typical Applications:

Typical applications for Types 201 are cookware, hose clamps, piston rings, transit car structural member, transit car roofing/siding, thermal window spacers, air bag containers, and truck trailer posts and door frames.

Chemical Composition:

ElementType 201
Carbon0.15x
Manganese5.5 – 7.5
Sulfur0.03X
Phosphorus0.060x
Silicon1.0 x
Chromium16 – 18
Nickel3.5 -5.5
Nitrogen0.25x

Mechanical Properties:

TypeYield Strength 0.2% offset (KSI)Tensile Strength (KSI)% Elongation
(2″ Gauge length)
201 Ann38 min.75 min.40% min.
201 ¼ Hard75 min.125 min.25.0 min.
201 ½ Hard110 min.150 min.18.0 min.
201 ¾ Hard135 min.175 min.12.0 min.
201 Full Hard145 min.185 min.9.0 min.

Physical Properties:

Density (lb./ in^2) @ RT 0.283
Modulus of Elasticity in Tension (psi x 10^6) 28.6
Specific Heat (BTU/o F/lb.)32 to 212 oF0.12
Thermal Conductivity (BTU/hr/ft^2/ft)212oF9.4
Mean Coefficient of Thermal Expansion (in. x 10^-6 per o F)32 to 212oF8.7
 32 to 600oF9.7
 32 to 1,000oF10.2
Electrical Resistivity (micro ohms – cm)at 70oF69
Melting Point Range (oF) 2550/2650
Oxidation Resistance – Continuous Service(oF) 1550
Oxidation Resistance – Intermittent Service(oF) 1500

Processing:

The annealing temperature for Type 201 is between 1850-2000°F. Rapid cooling through the carbide precipitation range (1500 – 800 o F) is necessary to keep the carbides in solution and prevent sensitization. Type 201 is not hardenable by thermal treatment; it is only hardenable by cold working.

Forming:

Type 201 has similar bending, forming and drawing characteristics to Type 301 stainless steel

Welding:

Type 201 can be welded by all conventional methods applied to 18 percent chromium, 8 percent nickel steels. Filler metal of the conventional chromium-nickel analyses can be used. Like other austenitic stainless steels where carbon is not controlled below 0.03%, Type 201 is susceptible to intergranular corrosion in the weld heat affected zone.

Corrosion:

Type 201 is resistant to a wide variety of mild to moderately corrosive environments. It has corrosion resistance approaching that of Types 301and has been successfully substituted for 304 in many mild environments.